Microstructural evolution of spray-formed Al-11.5Zn-2.0Mg-1.6Cu alloy during hot-extrusion and heat-treatment
GUO Shu(郭 舒), NING Zhi-liang(宁志良), CAO Fu-yang(曹福洋), SUN Jian-fei(孙剑飞)

School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China

Abstract:  Al-11.5Zn-2.0Mg-1.6Cu alloy was synthesized by spray forming (SF) technique followed by hot extrusion and heat-treatment. Its microstructural evolution was investigated by scanning electron microscopy (SEM), transmission electron microscopy (TEM) with energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD) in the whole process. The curve of hardness as a function of aging time was obtained at 120 ℃. Test results indicate that the grain morphology is equiaxed and uniform in the central region of the spray-formed billet, but fine and irregular in the bottom and top regions. Both the grain boundary and the intragranular phases are identified as MgZn2 intermetallics. Hot extrusion promotes the refinement of the microstructure. Grain boundary phase disappears, meanwhile, η-phase (MgZn2) and Al3Zr particles precipitate from the matrix after extrusion. The alloy reaches its maximum hardness after being aged at 120 ℃ for 14 h, associated with a massive precipitation of intermediate η′-phase (MgZn) in the matrix.

 

Key words:   Al-Zn-Mg-Cu alloy; spray forming; microstructure; hot extrusion; aging

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com