Isothermal solidification behavior of typical
Ni3Al base superalloy IC6①
WANG Xiao-ping(汪小平), ZHENG Yun-rong(郑运荣), XIAO Cheng-bo(肖程波),
WANG Bei-lei(王蓓蕾), HAN Ya-fang(韩雅芳)

Beijing Institute of Aeronautical Materials, Beijing 100095, P.R.China

Abstract:Solidification sequence of a typical Ni3Al base superalloy IC6 was studied by isothermal solidification method. The results show that the liquidus, solidus, melting point of the boride and secondaryγ′precipitation temperature of the IC6 alloy are notably higher than those of conventional nickel base superalloys because of its higher Mo content. There is no eutecticγ′precipitation during the solidification of the alloy, but a kind of Mo-richδ-Ni0.76Mo1.24primary phase precipitates together withγphase by eutectic reactionL′→δ+γ+L″in the temperature range of 1 573~1 553 K, thisδ- Ni0.76Mo1.24phase has a primitive orthorhombic structure witha=0.917 8 nm,b=0.914 2 nm andc=0.882 8 nm. Moreover, Al element of the alloy segregates in dendritic areas during isothermal solidification process, which causes secondaryγ′phase precipitate in the order of precedence from dendrites to interdendrites.


Key words: Ni3Al base superalloys; solidification process; microstructures;δ-Ni0.76Mo1.24phase

ISSN 1004-0609
CN 43-1238/TG

ISSN 1003-6326
CN 43-1239/TG

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱