Degradation characteristics of
Ti/(IrO2+Ta2O5) coating anodes in H2SO4solution①
HU Ji-ming(胡吉明), WU Ji-xun(吴继勋), MENG Hui-min(孟惠民),
SUN Dong-bai(孙冬柏), ZHU Yan-rong(朱艳冗), YANG De-jun(杨德钧)

Beijing Corrosion and Protection Center,
Open Laboratory of Corrosion, Erosion and Surface Technology,
University of Science and Technology Beijing, Beijing 100083, P.R.China

Abstract:The service life of Ti based IrO2+Ta2O5coating anodes over the whole composition range and prepared at different temperatures was studied by the accelerated electrolysis tests. The results show that as a result of incompleted decomposition, coatings obtained at low temperature are not stable. At the preparing temperature up to 450℃,the stability of the resulting deposits increase dramatically, and is independent on temperature. However, at higher temperature, oxidation of Ti base occurred leading to a decrease in the adhesion of coatings which resulted in decreasing of the service life of anodes. The maximum durability was obtained for the anodes prepared at 450℃.Resulting from the maximum solubility between the iridium and tantalum oxides, coatings with 70%IrO2+30%Ta2O5(mole fraction) exhibited the maximum stability. A preferential dissolution of Ir on the non-close-packed planes of the rutile oxides was observed for the pure IrO2deposits while on the close-packed planes for the IrO2and Ta2O5mixed ones in electrolysis. This dissolution characteristic can interpret a low service life for the coating anodes with a low IrO2content since the close-packed planes orientations are dominant in these flesh samples. Two mechanisms for the degradation of Ti/(IrO2+Ta2O5) anodes were also proposed.


Key words: oxide anodes; iridium oxide; tantalum oxide; degradation

ISSN 1004-0609
CN 43-1238/TG

ISSN 1003-6326
CN 43-1239/TG

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱