Influence of extrusion temperature on microstructure and
mechanical properties of Mg-4Y-4Sm-0.5Zr alloy
LI Da-quan(李大全)1, 2, WANG Qu-dong(王渠东)2, DING Wen-jiang(丁文江)2, J. J. BLANDIN3, M. SUÉRY3

1. National Engineering Research Center for Nonferrous Metals Composites,
General Research Institute for Nonferrous Metals, Beijing 100088, China;
2. National Engineering Research Center of Light Alloys Net Forming,
State Key Laboratory of Metal Matrix Composites, School of Materials Science and Engineering,
Shanghai Jiao Tong University, Shanghai 200240, China;
3. Université de Grenoble, Grenoble INP, Science et Ingénieriedes Matériaux et Procédés (SIMAP),
CNRS UMR 5266, UJF, BP 46, 38402 Saint-Martin d’Héres Cedex, France

Abstract:The solution-treated Mg-4Y-4Sm-0.5Zr alloy was extruded at temperatures from 325 ˚C to 500 ˚C. Dynamic recrystallization (DRX) completely occurs when the alloy is extruded at 350℃ and above. The grains of the extruded alloy are obviously refined by the occurrence of DRX. The average grain size of the extruded alloy increases with increasing the extrusion temperature, leading to a slight decrease of the ultimate tensile strength (UTS) and the yield strength (YS). On the contrary, the UTS and YS of the extruded and aged alloy increase with increasing the extrusion temperature. Values of UTS of 400 MPa, YS larger than 300 MPa and elongation (EL) of 7% are achieved after extrusion at 400 ˚C and ageing at 200 ˚C for 16 h. Both grain refinement and precipitation are efficient strengthening mechanisms for the Mg-4Y-4Sm-0.5Zr alloy.


Key words: Mg-Y-Sm-Zr alloy; extrusion; heat treatment; ageing; mechanical properties

ISSN 1004-0609
CN 43-1238/TG

ISSN 1003-6326
CN 43-1239/TG

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱