Thermal stability of nanocrystalline in surface layer of
magnesium alloy AZ91D
ZHANG Jin(张 津)1, 2, OU Xin-bing(欧信兵)2, 3

1. Institute of Advanced Material, University of Science and Technology Beijing, Beijing 100083, China;
2. College of Materials Science and Engineering, Chongqing University of Technology, Chongqing 400050, China;
3. Nanjing Kerun Lubricants Co., Ltd., Nanjing 211100, China

Abstract:Isothermal and isochronal annealing was conducted to study the thermal stability of the nanocrystalline in the surface layer of Mg alloy AZ91D induced by high-energy shot peening (HESP). Field emission scanning electron microscope (FESEM) and X-ray diffractometer were used to characterize the microstructure. Results showed that nanocrystalline produced by HESP on the surface layer of the magnesium alloy AZ91D was 60−70 nm on average. The nanocrystalline could remain stable at about 100 ˚C, and grew up slowly between 100 ˚C and 200 ˚C. When the annealing temperature reached 300 ˚C, the growth rate of the nanocrystalline increased significantly. The kinetic coefficient n of the nanocrystalline growth was calculated to be 2−3 and the grain growth activation energy Q=39.7 kJ/mol, far less than the self-diffusion activation energy of magnesium atoms in the coarse polycrystalline material.

 

Key words: high energy shot peening (HESP); magnesium alloy; AZ91D; nanocrystalline; thermal stability

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com