Cavity nucleation during hot forging of Ti-6Al-2Zr-1Mo-1V alloy with
colony alpha microstructure
DONG Xian-juan(董显娟)1, 2, LU Shi-qiang(鲁世强)1, ZHENG Hai-zhong(郑海忠)1,
LI Xin (李 鑫)1, OUYANG De-lai (欧阳德来)1

1. National Defense Key Disciplines Laboratory of Light Alloy Processing Science and Technology,
Nanchang Hangkong University, Nanchang 330063, China;
2. College of Materials Science and Technology, Nanjing University of
Aeronautics and Astronautics, Nanjing 210016, China

Abstract:The initiation sites and influencing factors of cavity nucleation were investigated for a Ti-6Al-2Zr-1Mo-1V alloy with lamellar starting structure, using the isothermal hot compression test. All samples were deformed to a true strain of 0.70 in the temperature range of 750−950 °C and strain rate range of 0.001−10 s−1. The corresponding microstructures were observed by means of the metallurgical microscopy and scanning electron microscopy (SEM). It was found that all cavities occurred at the bulge regions of the compression specimens. Most of cavities nucleated along prior beta boundaries oriented 45° to the compression axis, while others nucleated at the interfaces of lamellar alpha colonies. Cavity nucleation was inhibited with increasing the volume fraction of beta phase and the volume fraction spheroidized of lamellar alpha phase.


Key words: Ti-6Al-2Zr-1Mo-1V alloy; cavity nucleation; lamellar alpha colony; dynamic spheroidization

ISSN 1004-0609
CN 43-1238/TG

ISSN 1003-6326
CN 43-1239/TG

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱