Preparation and properties of flame-sprayed Mo-FeB-Fe cermet coatings
MA Zhuang1, WANG Wei1, 2, ZOU Ji-feng1, DONG Shi-zhi1, ZHANG Lian-yong1, LI Zhi-chao1

1. College of Materials Science and Engineering, Liaoning Technical University, Fuxin123000, China;
2. State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi’an 710072, China

Abstract:The powders of Mo2FeB2 cermet were prepared with Mo powders, Fe-B alloy powders and Fe powders as raw materials. Mo2FeB2 cermet coatings were prepared on Q235 steel by reactive thermal spraying (RTS) method and heated at 1 000 °C in vacuum oven of 1 kPa for 5 h. The properties of coatings were investigated. The results indicate that Fe2B appears after milling for 15 h in the powder at room temperature, a part of ternary borides (Mo2FeB2) are generated in powder sintered at 900 °C. The coatings are composed of the major phases Mo2FeB2 and α-Fe, a little of Fe2O3, FeO and some pores. The bonding strength between the substrate and the ceramic coating is 32.73 MPa, the thermal-shock times is about 43 and the wear resistance is enhanced by approximately 5.28 times compared with that of the substrate, respectively. The comprehensive properties of Mo2FeB2 cermet coatings can be improved further after vacuum heat-treatment at 1 000 °C for 5 h.


Key words: Mo2FeB2; cermet coating; reactive thermal spraying; hardness; thermal shock resistance; wear resistance

ISSN 1004-0609
CN 43-1238/TG

ISSN 1003-6326
CN 43-1239/TG

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱