Microstructure evolution and mechanical properties of ultrasonic-assisted soldering joints of 2024 aluminum alloys
LI Yuan-xing, ZHAO Wei-wei, LENG Xue-song, FU Qiu-jiao, WANG Lei, YAN Jiu-chun

State Key Laboratory of Advanced Welding Production Technology,
Harbin Institute of Technology, Harbin 150001, China

Abstract:Ultrasonic-assisted soldering of 2024 aluminum alloys using a filler metal of Zn-5Al alloy was investigated at the temperature of 400 °C, which is lower than the solution strengthening temperature of Al-Cu alloys. The ultrasonic vibration with  power of 200 W and vibration amplitude of 15 μm at the frequency of 21 kHz was applied on the top samples. The ultrasonic vibration promoted the dissolution of Al elements in the base metal. The reduction of volume fraction of the eutectic phases in the bonds was investigated by increasing ultrasonic vibration time. As the ultrasonic vibration time increased from 3 s to 30 s, the volume fraction of the eutectic phase in the bonds decreased from 12.9% to 0.9%, and the shear strength of the joints was up to 149−153 MPa, increased by 20%. The improvement of the mechanical properties of joints was discussed based on the modulus and hardness of the phases in the bonds and the fracture of the joints.

 

Key words: 2024 aluminum alloys; brazing; soldering; ultrasonic-assisted soldering; Zn-5Al filler metal

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com