Hot tearing susceptibility of Mg-xZn-2Y alloys
Zhi WANG1, Yi-zhou LI1, Feng WANG1, Yuan-ding HUANG2, Jiang-feng SONG2, Ping-li MAO1, Zheng LIU1

1. School of Materials Science and Engineering, Shenyang University of Technology, Shenyang 110870, China;
2. MagIC-Magnesium Innovation Centre, Helmholtz-Zentrum Geesthacht,
Max-Planck-Str. 1, Geesthacht 21502, Germany

Abstract:Effects of Zn content (0, 0.5%, 1.5% and 4.5%) on the hot tearing characteristics of Mg-2%Y alloy were studied in a constrained rod casting (CRC) apparatus attached with a load cell and data acquisition system. The experimental results indicate that the hot tearing susceptibility (HTS) is affected by the content of Zn. The Zn-free base alloy shows the lowest HTS. The HTS of Mg-xZn-2Y alloys increases with increasing Zn content, reaches the maximum at 1.5% Zn, and then decreases with further Zn addition. The high HTS observed in the alloy with 1.5% Zn is attributed to its high force release rate and large force drop during solidification. The hot cracks of casting are initiated and propagate along the dendritic or grain boundaries. The predictions of HTS of Mg-xZn-2Y alloys using ProCAST software are in good agreement with the results obtained by experimental measurements.

 

Key words: Mg-xZn-2Y alloy; hot tearing susceptibility; solidification contraction force; numerical simulation

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com