Hot deformation behaviors and processing maps of Mg-Zn-Er alloys based on Gleeble-1500 hot compression simulation
Cui-cui SUN, Ke LIU, Zhao-hui WANG, Shu-bo LI, Xian DU, Wen-bo DU

College of Materials Science and Engineering, Beijing University of Technology, Beijing 100124, China

Abstract:The hot deformation behaviors of as-solution Mg-xZn-yEr alloys (x/y=6, x=3.0, 4.5 and 6.0; y=0.50, 0.75 and 1.00) were investigated on Gleeble-1500 thermal simulator in a temperature range of 200-450 °C at a strain rate of 0.001-1 s-1. The true stress-strain curves showed the dynamic competition between the working hardening and working softening mainly due to the dynamic recrystallization (DRX) occurring during hot compression. The constitutive equations were constructed which could accurately predict the peak stress of the alloys. The addition of Zn and/or Er resulted in higher deformation activation energy for Mg-3Zn-0.5Er (alloy A). The processing maps were constructed as function of the temperature and the strain rate, providing the optimum hot working conditions (i.e., at strain of 0.3, Mg-3Zn-0.5Er (alloy A): 380-430 °C, <0.1 s-1; Mg-4.5Zn-0.75Er (alloy B): 380-450 °C, 0.01-0.1 s-1; Mg-6Zn-1Er (alloy C): 390-440 °C, 0.01-0.1 s-1). The as-solution treated Mg-4.5Zn-0.75Er (alloy B) demonstrated more optimum hot working window comparing with Mg-3Zn-0.5Er (alloy A) and Mg-6Zn-1Er (alloy C).


Key words: Mg-Zn-Er alloy; compression behavior; microstructure evolution; constitutive equations; processing map

ISSN 1004-0609
CN 43-1238/TG

ISSN 1003-6326
CN 43-1239/TG

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱