Effect of depressurizing speed on mold filling behavior and entrainment of oxide film in vacuum suction casting of A356 alloy
Shan-guang LIU1,2, Fu-yang CAO1,2, Jun-ying YI1,2,3, Xin-yi ZHAO1,2, Jing ZENG1,2, Zhi-liang NING1,2, Jian-fei SUN1,2

1. School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China;
2. National Key laboratory for Precision Hot Processing of Metals, Harbin Institute of Technology, Harbin 150001, China;
3. School of Metallurgical and Materials Engineering, Jiangsu University of Science and Technology, Zhangjiagang 215600, China

Abstract:The effect of depressurizing speed on mold filling behavior and entrainment of oxide film of A356 alloy was studied. The mold filling behavior and velocity fields were recorded by water simulation with particle image velocimetry. The results show that the gate velocity first increased dramatically, then changed with the depressurizing speed: the gate velocity increased slowly at relatively high depressurizing speed; at reasonable depressurizing speed, the gate velocity kept unchanged; while at lower depressurizing speed, the gate velocity decreased firstly and then kept unchanged. High gate velocity results in melt falling back under gravity at higher speed. The falling velocity is the main factor of oxide film entrainment in vacuum suction casting. The design criterion of depressurizing rate was deduced, and the A356 alloy castings were poured to test the formula. The four-point bend test and Weibull probability plots were applied to assessing the fracture mechanisms of the as-cast A356 alloy. The results illuminate a method on designing suitable depressurizing speed for mold filling in vacuum suction casting.

 

Key words: A356 aluminum alloy; vacuum suction casting; water simulation; surface turbulence; thin-walled casting; oxide film

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com