冷却速率对Ti-22Al-24Nb-0.5Mo合金显微组织和拉伸性能的影响
赵洪泽1, 2,卢 斌1,杨 锐1

(1. 中国科学院 金属研究所,沈阳 110016;
2. 中国科学技术大学 材料科学与工程学院,沈阳 110016
)

摘 要: 对Ti-22Al-24Nb-0.5Mo合金(摩尔分数,%)进行固溶后,分别以炉冷、空冷、油淬和水淬4种不同的冷却速率冷却到室温,再进行相同的时效处理,采用扫描电子显微镜(SEM)观察,发现空冷、油冷和水淬得到的显微组织为在B2/β相基体上析出弥散分布的α2相(等轴的和针状的)和细小的O相板条构成的双态组织,且发现随冷速增快,在冷却过程中析出的α2相减少,保留BCC相增加;炉冷时得到无序的β相,油冷时得到有序的B2相;4种冷却速率中,只有炉冷的过程中有O相析出;对不同冷却速率的试样进行性能测试,发现随冷速的增大,650 ℃的抗拉强度逐渐增大,室温的强度和塑性也有上升的趋势。

 

关键字: Ti2AlNb合金;冷却速率;显微组织;拉伸性能

Effect of cooling rate on microstructure and tensile properties of Ti-22Al-24Nb-0.5Mo alloy
ZHAO Hong-ze1, 2, LU Bin1, YANG Rui1

1. Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China;
2. School of Materials Science and Engineering, University of Science and Technology of China, Shenyang 110016, China

Abstract:The effect of cooling rate on the microstructure and tensile properties of Ti-22Al-24Nb-0.5Mo (mole fraction, %) alloy was studied. Cooling from 980 ℃ to room temperature was arranged by four kinds of rate, including furnace cooling, air cooling, oil quenched and water quenched, and then followed by the same aging treatment. The results show that the multiphase structure consists of dispersively distributed α2 (equiaxed and acicular) phase, fine O phase and B2/β phase matrix by air cooling, oil quenching and water quenching. The volume fraction of α2 phase reduces and the volume fraction of BCC phase increases with increasing the cooling rate. The disorder β phase is formed at furnace cooling, the order B2 phase is obtained at oil quenched. The strength at 650 ℃ increases with the cooling rate increasing, which is similar to that at room temperature.

 

Key words: Ti2AlNb alloy; cooling rate; microstructure; tensile property

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com