Transactions of Nonferrous Metals Society of China

Vol. 28    No. 6    June 2018

[PDF Download]        

    

Effect of Si addition and applied pressure on microstructure and tensile properties of as-cast Al-5.0Cu-0.6Mn-1.2Fe alloys
Wei-wen ZHANG, Yu-liang ZHAO, Da-tong ZHANG, Zong-qiang LUO, Chao YANG, Yuan-yuan LI

National Engineering Research Center of Near-net-shape Forming for Metallic Materials, South China University of Technology, Guangzhou 510641, China

Abstract:The effects of Si addition and applied pressure on the microstructure and tensile properties of as-cast Al-5.0Cu-0.6Mn- 1.2Fe alloys were studied. The results show that Si addition promotes the formation of Chinese script α-Fe, and suppresses the precipitation of Al3(FeMn) and Al6(FeMn). For the alloys produced without pressure, Si addition increases the volume fraction of porosity, resulting in remarkable decrease in ultimate tensile strength (UTS) and yield strength (YS). For the alloys produced with 75 MPa pressure, Si addition improves UTS and YS owing to the formation of high number density of Al2Cu (θ) phases. The tensile properties of alloys increase with increasing applied pressure at the same Si content level, which is attributed to elimination of porosity, grain refinement strengthening and solid-solution strengthening. The alloy with 1.1% Si addition and 75 MPa pressure shows the best tensile properties, where the UTS, YS and elongation are 237 MPa, 140 MPa and 9.8%, respectively.

 

Key words: Al-Cu alloys; Si addition; solidification; tensile properties; microstructure

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com