Vol. 28    No. 12    December 2018

[PDF Download]    [Flash Online]    

    

Bonding strength of Invar/Cu clad strips fabricated by twin-roll casting process
Peng CHEN1,2, Hua-gui HUANG1,2, Ce JI1,2, Xu ZHANG1,2, Zhong-hua SUN3

1. National Engineering Research Center for Equipment and Technology of Cold Strip Rolling, Yanshan University, Qinhuangdao 066004, China;
2. College of Mechanical Engineering, Yanshan University, Qinhuangdao 066004, China;
3. Iron and Steel Research Institute of HBIS Group, Shijiazhuang 052165, China

Abstract:Based on traditional twin-roll casting process, Invar/Cu clad strips were successfully fabricated by using solid Invar alloy strip and molten Cu under conditions of high temperature, high pressure and plastic deformation. A series of tests including tensile test, bending test, T-type peeling test and scanning electron microscope (SEM) and energy dispersive spectrometer (EDS) measurements were carried out to analyze the mechanical properties of Invar/Cu clad strips and the micro-morphology of tensile fracture surfaces and bonding interfaces. The results indicate that no delamination phenomenon occurs during the compatible deformation of Invar/Cu in bending test and only one stress platform exists in the tensile stress-strain curve when the bonding strength is large. On the contrary, different mechanical properties of Invar and Cu lead to delamination phenomenon during the uniaxial tensile test, which determines that two stress platforms occur on the stress-strain curve of Invar/Cu clad strips when two elements experience necking. The average peeling strength can be increased from 13.85 to 42.31 N/mm after heat treatment at 800 °C for 1 h, and the observation of the Cu side at peeling interface shows that more Fe is adhered on the Cu side after the heat treatment. All above illustrate that heat treatment can improve the strength of the bonding interface of Invar/Cu clad strips.

 

Key words: twin-roll casting; Invar/Cu clad strip; heat treatment; bonding interface; bonding strength

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com