Hot cracking tendency test and simulation of 7075 semi-solid aluminium alloy
Bing ZHOU, Shuai LU, Kai-le XU, Chun XU, Zhan-yong WANG, Bin-jun WANG

School of Materials Science and Engineering, Shanghai Institute of Technology, Shanghai 201418, China

Abstract:The hot cracking tendency of 7075 semi-solid alloy under different conditions was studied by critical diameter method. The experiment and simulation results show that the dendrite arms of the rod grow from the edge to the center. The smaller the diameter of the rod is, the more obvious the directional growth of dendrite is, and the greater the tendency of hot cracking is. Compared with ordinary melt, for semi-solid slurry, increasing mould temperature or decreasing pouring temperature can significantly decrease hot cracking tendency of 7075 alloy, decreasing hot cracking grade from 256 to 100 mm2. Furthermore, based on the RDG criterion, the effects of solidification conditions on the hot cracking tendency were discussed combined with simulation. At the same time, the application and development of RDG criterion were also researched.

 

Key words: hot cracking tendency; semi-solid slurry; 7075 aluminium alloy; RDG criterion; numerical simulation

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com