Constitutive modeling of flow behavior of precipitation-hardened AA7022-T6 aluminum alloy at elevated temperature
H. R. REZAEI ASHTIANI, P. SHAHSAVARI

School of Mechanical Engineering, Arak University of Technology, Arak, Iran

Abstract:The thermomechanical behavior of precipitation-hardened aluminum alloy AA7022-T6 was studied using isothermal compression at temperatures of 623-773 K and strain rates of 0.01-1 s-1. The experimental results indicated that dynamic recrystallization (DRX) is a predominant hot deformation mechanism, especially at elevated temperatures and low strain rates. The modified Johnson-Cook (J-C) and the strain compensated Arrhenius-type models were developed to predict the hot flow behavior under different deformation conditions. The correlation coefficients of modified J-C model and the strain compensated Arrhenius-type models were 0.9914 and 0.9972, respectively, their average relative errors (ARE) were 6.074% and 4.465%, respectively, and their root mean square errors (RMSE) were 10.611 and 1.665 MPa, respectively, indicating that the strain compensated Arrhenius-type model can predict the hot flow stress of AA7022-T6 aluminum alloy with an appropriate accuracy.

 

Key words: flow behavior; constitutive models; Arrhenius model; dynamic recrystallization; AA7022-T6 aluminum alloy

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com