Microstructure and mechanical properties of 7005 aluminum alloy processed by one-pass equal channel reciprocating extrusion
Ju-fu JIANG1, Ying WANG2, Ying-ze LIU1, Guan-fei XIAO1, Hua LI2

1. School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China;
2. School of Mechatronics Engineering, Harbin Institute of Technology, Harbin 150001, China

Abstract:An equal channel reciprocating extrusion (ECRE) was proposed first to obtain a severe plastic deformation (SPD) of 7005 alloy. The microstructure and mechanical properties of one-pass ECREed (ECRE processed) 7005 alloy were investigated. The results show that SPD occurring in ECRE leads to a mixed microstructure. ECREed 7005 alloy exhibits a significant improvement of ultimate tensile strength (UTS) and elongation. Mechanical properties in the region undergoing a complete ECRE process are higher than those in the region undergoing an incomplete ECRE process due to larger dislocation strengthening effect. Yield strength (YS) and UTS first decrease and then increase with an increase of extrusion temperature. The YS of 359.2 MPa, UTS of 490 MPa and elongation of 17.7% are obtained after T6 treatment. Fine-grain strengthening, dislocation strengthening and precipitation strengthening in the T6-treated ECREed sample all play important roles in improving the mechanical properties.


Key words: 7005 aluminum alloy; equal channel reciprocating extrusion; microstructure; mechanical properties

ISSN 1004-0609
CN 43-1238/TG

ISSN 1003-6326
CN 43-1239/TG

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱