Experiment and modeling of TiB2/TiB boride layer of Ti-6Al-2Zr-1Mo-1V alloy
De-lai OUYANG1, Sheng-wei HU1, Cheng TAO1, Xia CUI1, Zhi-shou ZHU2, Shi-qiang LU1

1. Key Laboratory for Microstructural Control of Metallic Materials of Jiangxi Province, Nanchang Hangkong University, Nanchang 330063, China;
2. Beijing Institute of Aeronautical Materials, Beijing 100095, China

Abstract:The influence of the boriding conditions on the boride layers was examined by boriding Ti-6Al-2Zr- 1Mo-1V alloy in the temperature range of 920-1120 °C. The experimental results show that the boride layers were composed of a continuous thin outer layer of TiB2 and a thick inner layer of TiB with whiskers or needle-like morphologies that extended into the substrate. Thick and compact boride layers were obtained when the boriding temperatures were 1000-1080 °C, and the treatment time exceeded 8 h. The boride layer depth increased with the boriding temperature and time, and the growth kinetics of the boride layers was characterized by a parabolic curve. The growth kinetics of the boride layers, including both TiB2 and TiB layers, were predicted by establishing a diffusion model, which presented satisfactory consistency with the experimental data. As a result, the activation energies of boron in the TiB2 and TiB layers were estimated to be 223.1 and 246.9 kJ/mol, respectively.

 

Key words: Ti-6Al-2Zr-1Mo-1V alloy; boriding; microstructure; modeling

ISSN 1004-0609
CN 43-1238/TG
CODEN: ZYJXFK

ISSN 1003-6326
CN 43-1239/TG
CODEN: TNMCEW

主管:中国科学技术协会 主办:中国有色金属学会 承办:中南大学
湘ICP备09001153号 版权所有:《中国有色金属学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市岳麓山中南大学内 邮编:410083
电 话:0731-88876765,88877197,88830410   传真:0731-88877197   电子邮箱:f_ysxb@163.com